Composition and Classification of Dental Porcelain
- Dental porcelain is composed of materials such as kaolin, quartz, feldspar, metallic colorants, and glass.
- The composition of dental feldspathic porcelain typically includes 3-5% kaolin, 12-25% quartz, 70-85% feldspar, 1% metallic colorants, and up to 15% glass.
- Dental ceramics can be classified based on the microstructure of the ceramics, including glass-based systems (e.g., feldspathic porcelain), glass-based systems with fillers (e.g., leucite or lithium disilicate), crystalline-based systems with glass fillers (e.g., alumina), and polycrystalline solids (e.g., alumina and zirconia).
Firing and Glazing of Dental Porcelain
- Firing is the process of heating the dental porcelain to allow the ceramic particles to fuse and form the final restoration.
- Multiple rounds of firing may be required to build up the restoration to the desired shape and size.
- The first firing removes water and allows the particles to coalesce, resulting in shrinkage.
- Slow cooling after firing is necessary to prevent cracking and maintain the strength of the restoration.
- Glazing is the final stage of sealing the surface of the dental porcelain, creating a smooth finish.
- Glazing can be achieved by re-firing the restoration or using glazes with lower fusing temperatures.
- It fills porous areas and prevents wear on opposing teeth.
- Adjustments to the restoration can be made with polishing rubbers and fine diamonds after glazing.
Staining of Dental Porcelain
- Dental porcelain can be stained to enhance tooth morphology, such as occlusal fissures and hypoplastic spots.
- Stains can be incorporated within the ceramic or applied onto the surface.
Properties and Applications of Dental Porcelain
- Dental porcelain exhibits excellent esthetics, closely resembling natural teeth.
- It has high biocompatibility and does not cause adverse reactions in the oral cavity.
- Porcelain restorations are resistant to staining and discoloration.
- They have good mechanical properties, providing strength and durability.
- Porcelain can be customised to match the color, shape, and size of the patient's natural teeth.
- Dental porcelain is commonly used for fabricating crowns, veneers, inlays, onlays, and bridges.
- Porcelain can be layered onto a metal framework to create porcelain-fused-to-metal restorations.
- All-ceramic restorations, where the entire restoration is made of porcelain, are gaining popularity.
- Dental implants can be restored with porcelain crowns or bridges for a natural appearance.
Challenges, Limitations, and Advances in Dental Porcelain
- Porcelain restorations require precise fabrication techniques and skilled dental laboratory technicians.
- The brittleness of porcelain makes it prone to fracture under high stress.
- Adjustments and repairs to porcelain restorations can be challenging and may require expertise.
- Porcelain restorations may cause excessive wear on opposing natural teeth.
- The cost of porcelain restorations can be higher compared to other dental materials.
- New materials and processing methods are being developed to improve the properties of dental porcelain.
- CAD/CAM technology enables the fabrication of precise and esthetic porcelain restorations.
- Digital dentistry is revolutionizing the design and production of porcelain restorations.
- Research is focused on enhancing the strength and fracture resistance of porcelain materials.
- The integration of nanotechnology in dental porcelain may lead to further advancements in its properties and applications.
Dental porcelain (also known as dental ceramic) is a dental material used by dental technicians to create biocompatible lifelike dental restorations, such as crowns, bridges, and veneers. Evidence suggests they are an effective material as they are biocompatible, aesthetic, insoluble and have a hardness of 7 on the Mohs scale. For certain dental prostheses, such as three-unit molars porcelain fused to metal or in complete porcelain group, zirconia-based restorations are recommended.
The word "ceramic" is derived from the Greek word κέραμος keramos, meaning "potter's clay". It came from the ancient art of fabricating pottery where mostly clay was fired to form a hard, brittle object; a more modern definition is a material that contains metallic and non-metallic elements (usually oxygen). These materials can be defined by their inherent properties including their hard, stiff, and brittle nature due to the structure of their inter-atomic bonding, which is both ionic and covalent. In contrast, metals are non-brittle (display elastic behavior), and ductile (display plastic behaviour) due to the nature of their inter-atomic metallic bond. These bonds are defined by a cloud of shared electrons with the ability to move easily when energy is applied. Ceramics can vary in opacity from very translucent to very opaque. In general, the more glassy the microstructure (i.e. noncrystalline) the more translucent it will appear, and the more crystalline, the more opaque.